PLASCO DATA SHEET
SOQUEL, CA., 95073
TYPICAL PROPERTIES
831-464-1111       831-464-1100 (FAX)

 

MATERIAL:  P-T-100B
GENERIC:  ABS BK.
 
 

ASTM TEST METHODS VALUE
SPECIFIC GRAVITY: D-792  g/cm3 1.04
WATER ABSORPTION: D-570  24hrs %
MOLD SHRINK FLOW: D-955  in/in .005
MOLD SHRINK TRANS: D-955  in/in .007
TENSILE STRENGTH: D-638   psi  6000
TENSILE ELONGATION: D-638  %
FLEXURAL STRENGTH: D-790  psi 10500
FLEXURAL MODULUS: D-790   psi 340000
COMPRESSIVE STRENGTH: D-695  psi
IZOD NOTCHED: D-256  ft-lb/in 6.5
IZOD UNNOTCHED: D-256   ft-lb/in
HARDNESS: D-785 R103


CO. LINEAR THERM.EXP: D-696  10(-5) "/"F
THERMAL COND: C-177 btu-ft2/hr"F
DEFORMATION UNDER LOAD: D-621   %
HDT 66: D-648  F 203
HDT 264: D-648  F 188
FLAMMABILITY: UL  SUBJECT 94 HB


5 KV DECAY RATE: MIL-B-81705B
SURFACE RESISTIVITY: ohm/sq.
VOLUME RESISTIVITY: ohm-cm.


WEAR FACTOR: 10(-10)in3min/ft/lb/hr 3500
STATIC FRICTION: 40psi 0.30
DYNAMIC FRICTION: 40psi  50fpm 0.35
LPV 10FPM: psi  fpm 
LPV 100FPM: psi  fpm


MELT TEMP: F 400-475
MOLD TEMP: F 80-160
CYLINDER TEMPS: F 400-500
DRYING TEMP: F 180-200
DRYING TIME: HRS 2
This information is based on our experience to date and we believe it to be reliable. It is intended only as a guide for use at your discretion & risk. We cannot guarantee favorable results and assume no liability in connection with its use. None of this information is to be taken as a license to operate under, or a recommendation to infringe, any patents.